3D Printing Materials
Photocentric manufacture a range of functional resins for a wide variety of applications.
We are a vertically integrated chemical manufacturer, reacting hundreds of tonnes of polymers through to formulating resins.
3D Printing Materials
Photocentric manufacture a range of functional resins for a wide variety of applications.
We are a vertically integrated chemical manufacturer, reacting hundreds of tonnes of polymers through to formulating resins.
Durable DL110H
Impact and compression resistant grade that allows some bending and stress fatigue without breaking or deforming.
Applications
Jigs and fixtures requiring minimal deflection at elevated temperatures, cover plates and enclosures, fastenings, tools and couplings, strong and stiff prototypes, props.
Compatible Printers
5kg from
£300.00 excl vat
Volume discounts available
Rigid DLFR
Rigid DLFR has UL 94 V-0 certification, even showing self-extinguishing properties in the green state. It exhibits exceptionally high HDT and high tensile modulus.
Applications
Any application requiring durable rigid flame-retardant properties, for instance electrical enclosures and connectors, high power electrical appliances and battery housings.
Compatible Printers
5kg from
£252.45 - £375.00 excl vat
Volume discounts available
Rigid UVFR
Rigid UVFR has UL 94 V-0 certification, even showing self-extinguishing properties in the green state. It exhibits exceptionally high HDT and high tensile modulus.
Applications
Any application requiring durable rigid flame-retardant properties, for instance electrical enclosures and connectors, high power electrical appliances and battery housings.
Compatible Printers
1kg from
£50.49 - £75.00 excl vat
Volume discounts available
High Temp DL401
Rigid, high temperature material possessing high
stiffness and ductility.
Applications
Hot fluid and gas manifolds, moulds and inserts, heat resistant housings and fixtures
Compatible Printers
5kg from
£252.45 - £375.00 excl vat
Volume discounts available
High Temp DL400
Extremely high operating temperatures of up to 230°C without bending or deforming, simulating the properties of glass filled Nylon 6.
Applications
Hot fluid and gas manifolds, moulds and inserts, heat resistant housings and fixtures.
Compatible Printers
5kg from
£252.45 - £375.00 excl vat
Volume discounts available
Elastic DL160
High energy dampening at room and even low temperatures (-25 °C) with rebound resilience of 10%, 90% of energy is absorbed.
Applications
Sportswear protection and helmets, cold temperature flexibility, dampening rubbers and foams, gaskets and seals
Compatible Printers
5kg from
£252.45 - £375.00 excl vat
Volume discounts available
Magna Hard
Very high green strength and low shrinkage make this a reliable grade for printing. Cured parts exhibit extreme hardness with little compression under force.
Applications
Functional end use and prototype parts.
Compatible Printers
5kg from
£168.30 - £250.00 excl vat
Volume discounts available
High Tensile UV
Ideal for making objects with a high tensile strength and hardness that cannot be bent or compressed easily..
Applications
Prototyping and functional engineering
Compatible Printers
1kg from
£33.66 - £50.00 excl vat
Volume discounts available
Rigid DL240 Plant-Based
Rigid tough material with over 50% plant based raw materials, offering a substantial reduction in embedded Carbon.
Applications
Fast prototyping, accurate parts, dental models for aligner manufacturing.
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
Rigid UV240 Plant-Based
Rigid tough material with over 50% plant based raw materials, offering a substantial reduction in embedded Carbon.
Applications
Fast prototyping, accurate parts, dental models for aligner manufacturing.
Compatible Printers
1kg from
£40.39 - £60.00 excl vat
Volume discounts available
Durable UV80
Tough, functional parts that are durable, long-lasting and have high impact strength.
Applications
Jigs and fixtures, cover plates and enclosures and end-use parts.
Compatible Printers
1kg from
£50.49 - £75.00 excl vat
Volume discounts available
Magna Duramax
Functional durable parts with high impact strength.
Applications
Jigs and fixtures requiring minimal deflection, cover plates and enclosures, fastenings, tools and couplings.
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
UV Basics
The first choice for low-cost, accurate printing. The zero-irritancy and low odour make printing and post-processing safer and easier.
Applications
End use, fast prototyping and accurate models
Compatible Printers
1kg from
£19.99 excl vat
Flexible DL220B
Combines impact absorption, high elongation, efficient energy damping, good tear strength and very low water absorption
Applications
Sport protection helmets, shock absorption, phone cases, cushioning
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
Ultracur3D® EPD1006
Functional parts capable of movement and flexibility without breaking.
Applications
Functional engineering parts and prototyping
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
Ultracur3D® EPD1086
Multi-purpose grade with balanced mechanical properties.
Applications
Engineering and prototype parts
Compatible Printers
5kg from
£168.30 - £250.00 excl vat
Volume discounts available
Ultracur3D® EPD2006
Rigid, durable and long-lasting material which delivers the finest detail possible.
Applications
Engineering and prototyping parts requiring resilience with some compression
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
Ultracur3D® EPD3500
Strong translucent daylight resin with superior strength and stiffness.
Applications
Functional engineering parts and prototyping
Compatible Printers
5kg from
£252.45 - £375.00 excl vat
Volume discounts available
Magna Dental Model
Creates highly accurate, high-resolution models ideal for thermoforming orthodontic models for aligner manufacture.
Applications
Orthodontic models
Compatible Printers
5kg from
£300.00 excl vat
Volume discounts available
Dental Model UV
Creates highly accurate, high-resolution models ideal for thermoforming orthodontic models for aligner manufacture.
Applications
Orthodontic models
Compatible Printers
1kg & 5kg from
£60.00 – £300.00 excl vat
Volume discounts available
Magna Draft
Our fastest printing resin comparable to acrylic and polyamides.
Applications
Rapid prototyping
Compatible Printers
5kg from
£201.95 - £300.00 excl vat
Volume discounts available
Flexible UV160
Highly elastic stiff 3D resin with an 86A shore hardness suitable for end user functional parts, presenting TPU properties.
Applications
Seals, gaskets, grips and handles, cushioning, footwear
Compatible Printers
1kg from
£50.49 - £75.00 excl vat
Volume discounts available
Hard UV
Very high green strength and low shrinkage make this a reliable grade for printing. Cured parts exhibit extreme hardness with little compression under force.
Applications
Functional parts, prototypes, compression-resisting parts
Compatible Printers
1kg
£27.50 – £50.00 excl vat
Volume discounts available
Photocentric Resin Cleaner 30
Photocentric Resin Cleaner 30 has been optimally formulated to remove photopolymer resin, rapidly cleaning even the most intricate, detailed parts. It reduces post curing times and leaves parts shiny and dry to touch.
£66.50 – £252.20 excl vat
5L & 20L available
Left part washed with IPA vs right part washed with resin cleaner
DL110H – Material Properties
2100 MPa
Tensile Modulus – ASTM D638
86 Shore D
Hardness – ASTM D2240
54 MPa
Ultimate Tensile Strength – ASTM D638
75°C
Heat Deflection Temperature – ASTM D648
28%
Elongation at break – ASTM D638
0.62%
Water Absorption (Short Term) – 1 x 1 x 1 cm3 cube
1950 MPa
Flexural Modulus – ASTM D790
480 cPs
Viscosity – At 25°C Brookfield spindle 3
78 MPa
Flexural Strength – ASTM D790
1.14 g/cm3
Density
110 J/m
Impact Strength Notched Izod – ASTM D256
10<T<50°C
Storage
Mechanical properties stated based on fully cured material.
Colours:
Black 
Translucent
Technical & Safety Data Sheets
Select your resin and language below
High Temp DL401 – Material Properties
3180 MPa
Tensile Modulus – ASTM D638
3.5
Relative Permittivity, 20°C
77 MPa
Ultimate Tensile Strength – ASTM D638
4.05
Relative Permittivity, 100°C
4.8%
Elongation at break – ASTM D638
30 x 10-3
Dielectric Loss Factor, 20°C
3240 MPa
Flexural Modulus – ASTM D790
31 x 10-3
Dielectric Loss Factor, 100°C
123 MPa
Flexural Strength – ASTM D790
92 D
Hardness – ASTM D2240
16 J/m
Impact Strength Notched Izod – ASTM D256
270°C
Heat Deflection Temperature – ASTM D648 (0.45 MPa)
0.20 W/(m.K)
Thermal Conductivity, 23°C – ASTM D7984
0.28 wt%
Water Absorption (Short Term) – ASTM D570
0.21 W/(m.K)
Thermal Conductivity, 100°C – ASTM D7984
700 cPs
Viscosity – At 25°C Brookfield spindle 3
1.36 J/(g.K)
Specific Heat Capacity, 23°C – ASTM D7984
1.1 g/cm3
Density
1.69 J/(g.K)
Specific Heat Capacity, 100°C – ASTM D7984
10<T<50°C
Storage
Mechanical properties stated based on fully cured material. Post cured for 2hrs at 60°C in Cure L2 or Cure XL
Colours:
TranslucentHigh Temp DL400 – Material Properties
4000 MPa
Tensile Modulus – ASTM D638
95 Shore D
Hardness – ASTM D2240
80 MPa
Ultimate Tensile Strength – ASTM D638
230°C
Heat Deflection Temperature – ASTM D648 (0.455 MPa)
4%
Elongation at break – ASTM D638
0.35%
Water Absorption (Short Term) – ASTM D570
3300 MPa
Flexural Modulus – ASTM D790
650 cPS
Viscosity – At 25°C Brookfield spindle 3
109 MPa
Flexural Strength – ASTM D790
1.10 g/cm3
Density
15.8 J/m
Impact Strength Notched Izod – ASTM D256
10<T>50°C
Storage
3.1 kJ/m2
Impact Strength Notched Izod – ISO 180
Passed
Cytotoxicity – ISO 10993-5
Mechanical properties stated based on fully cured material.
Colours:
TranslucentElastic DL160 – Material Properties
13 MPa
Tensile Modulus – ASTM D412
70 Shore A
Hardness – ASTM D2240
12 MPa
Tensile Strength (Break) – ASTM D412
-24 °C
Tg (DSC, S1 –57, S2 8)
2 MPa
Tensile strength @ 50% Elongation – ASTM D412
0.34%
Water absorption (%)* after 24 hrs – ASTM D570
4 MPa
Tensile strength @ 100% Elongation- ASTM D412
0.38%
Water absorption (%)* after 72 hrs – ASTM D570
8 MPa
Tensile strength @ 150% Elongation- ASTM D412
0.56%
Water absorption (%)* after 7 days – ASTM D570
162%
Elongation at Break – ASTM D412
1100 cPs
Viscosity – At 25°C Brookfield spindle 3
20 kN/m
Tear Strength – ASTM 624
1.04 g/cm3
Density
10%
Rebound Resilience – ASTM D7121
10<T<
Storage
Post cured for 2 hours at 60°C with Photocentric Cure L2
Colours:
Translucent
Magna Hard – Material Properties
2600 MPa
Tensile Modulus – ASTM D638
55 J/m
Impact Strength Notched Izod – ASTM D256
52 MPa
Ultimate Tensile Strength – ASTM D638
86 Shore D
Hardness – ASTM D2240
10%
Elongation at break – ASTM D638
85°C
Heat Deflection Temperature – ASTM D648
1550 MPa
Flexural Modulus- ASTM D790
450 cPs
Viscosity – At 25°C Brookfield spindle 3
65 MPa
Flexural Strength – ASTM D790
1.1 g/cm3
Density
10<T>
Storage
Mechanical properties stated based on fully cured material.
Colours:
BlackHigh Tensile UV – Material Properties
2610 MPa
Tensile Modulus – ASTM D638
80 Shore D
Hardness – ASTM D2240
65 MPa
Ultimate Tensile Strength – ASTM D638
63°C
Heat Deflection Temperature – ASTM D648
6%
Elongation at break – ASTM D638
510 cPs
Viscosity – At 25°C Brookfield spindle 3
1910 MPa
Flexural Modulus- ASTM D790
1.16 g/cm3
Density
8.1 kJ/m2
Impact Strength Notched Izod – ISO 180
10<T>50°C
Storage
Mechanical properties stated based on fully cured material.
Colours:
GreyRigid DL240 – Material Properties
2440 MPa
Tensile Modulus – ASTM D638
88 Shore D
Hardness – ASTM D2240
56.6 MPa
Tensile Strength (Break) – ASTM D638
78.4°C
HDT (@ 0.455 MPa) – ASTM D648
64.5 MPa
Tensile Strength (Yield) – ASTM D638
62.6°C
HDT (@ 1.82 MPa) – ASTM D648
6.1%
Elongation at Break – ASTM D638
0.470%
Water absorption (%)* after 24 hrs – ASTM D570
108 MPa
Flexural Strength – ASTM D790
0.625%
Water absorption (%)* after 72 hrs – ASTM D570
2656
Flexural Modulus – ASTM D790
0.933%
Water absorption (%)* after 7 days – ASTM D570
12.2 J/m
Impact Strength Notched Izod – ASTM 256
580 cPs
Viscosity – At 25°C Brookfield spindle 3
2.2 kJ/m2
Impact Strength Notched Izod – ISO 180
1.10 g/cm3
Density
10<T>50°C
Storage
Mechanical properties based on post curing for 2 hours at 60°C with Photocentric Cure L2
Colours:
Translucent
Rigid UV240 – Material Properties
2080 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
52 MPa
Tensile Strength (Break) – ASTM D638
78.4°C
HDT (@ 0.455 MPa) – ASTM D648
54 MPa
Tensile Strength (Yield) – ASTM D638
62.6°C
HDT (@ 1.82 MPa) – ASTM D648
5.4%
Elongation at Break – ASTM D638
0.470%
Water absorption (%)* after 24 hrs – ASTM D570
108 MPa
Flexural Strength – ASTM D790
0.625%
Water absorption (%)* after 72 hrs – ASTM D570
2656
Flexural Modulus – ASTM D790
0.933%
Water absorption (%)* after 7 days – ASTM D570
12.2 J/m
Impact Strength Notched Izod – ASTM 256
580 cPs
Viscosity – At 25°C Brookfield spindle 3
2.2 kJ/m2
Impact Strength Notched Izod – ISO 180
1.10 g/cm3
Density
10<T>50°C
Storage
Mechanical properties based on post curing for 2 hours at 60°C with Photocentric Cure M+
Colours:
TranslucentDurable UV80 – Material Properties
1940 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
46 MPa
Ultimate Tensile Strength – ASTM D638
65°C
Heat Deflection Temperature
13%
Elongation at break – ASTM D638
400 cPs
Viscosity – At 25°C Brookfield spindle 3
28 MPa
Flexural Strength – ASTM D790
1.10 g/cm3
Density
760 MPa
Flexural Modulus – ASTM D790
10<T>
Storage
8.1 kJ/m2
Impact Strength Notched Izod – ISO 180
Magna Duramax – Material Properties
1760 MPa
Tensile Modulus – ASTM D638
70 Shore D
Hardness – ASTM D2240
50 MPa
Ultimate Tensile Strength – ASTM D638
60°C
Heat Deflection Temperature – ASTM D648
19%
Elongation at break – ASTM D638
1.4%
Water Absorption (Short Term) – ASTM D570
1600 MPa
Flexural Modulus – ASTM D790
395 cPs
Viscosity – At 25°C Brookfield spindle 3
70 MPa
Flexural Strength – ASTM D790
1.11 g/cm3
Density
51 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Storage
5.4 kJ/m2
Impact Strength Notched Izod – ISO 180
UV Basics – Material Properties
2330 MPa
Tensile Modulus – ASTM D638
110°C
Heat Deflection Temperature – ASTM D648
57.8 MPa
Ultimate Tensile Strength – ASTM D638
0.1%
Water absorption (%) after 24 hrs
6%
Elongation at break – ASTM D638
1.4%
Water absorption (%) after 72 hrs
2190 MPa
Flexural Modulus – ASTM D790
0.6%
Water absorption (%) after 7 days
86.6 MPa
Flexural Strength – ASTM D790
740 cPs
Viscosity – At 25°C Brookfield spindle 3
42.4 J/m
Impact Strength Notched Izod – ASTM D256
1.10 g/cm3
Density
87 Shore D
Hardness – ASTM D2240
10<T>
Storage
Flexible DL220B – Material Properties
66.4 MPa
Tensile Modulus – ASTM D412
0.32%
Water absorption (%) after 24 hrs – ASTM D570
14 MPa
Tensile Strength (Break) – ASTM D412
0.53%
Water absorption (%) after 72 hrs – ASTM D570
211%
Elongation at break – ASTM D412
1.09%
Water absorption (%)* after 7 days – ASTM D570
21 kN/m
Tear Strength – ASTM 624 Type C
1600 cPs
Viscosity – At 25°C Brookfield spindle 3
19.6%
Rebound Resilience – ASTM D7121
1.06 g/cm3
Density
42.4 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Storage
80 Shore A
Hardness – ASTM D2240
Ultracur3D® EPD 1006 – Material Properties
1033 mPas
Viscosity 30 °C – Cone/Plate Rheometer
20 J/m
Notched Izod (Machined), -30 °C – ASTM D256
268 mPas
Viscosity 50 °C – Cone/Plate Rheometer
35 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1.2 g/cm3
Density (printed part) – ASTM D792
2.5 kJ/m2
Charpy notched, 23 °C – ISO 179-1
1500 MPa
E Modulus – ASTM D638
44°C
HDT at 0.45 MPa – ASTM D648
40 MPa
Ultimate Tensile Strength – ASTM D638
40°C
HDT at 1.82 MPa – ASTM D648
25%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
1460 MPa
Flexural Modulus – ASTM D790
0.83 %
Water Absorption, Short Term (24 hours) – ASTM D570
52 MPa
Flexural Strength – ASTM D790
79 Shore D
Hardness – ASTM D2240
Ultracur3D® EPD 1086 – Material Properties
450 mPas
Viscosity 30 °C – Cone/Plate Rheometer
28 J/m
Notched Izod (Machined), 23 °C – ASTM D256
130 mPas
Viscosity 50 °C – Cone/Plate Rheometer
606 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1.18 g/cm3
Density (printed part) – ASTM D792
2.6 kJ/m2
Charpy notched, 23 °C – ISO 179-1
1810 MPa
E Modulus – ASTM D638
53°C
HDT at 0.45 MPa – ASTM D648
42 MPa
Ultimate Tensile Strength – ASTM D638
46°C
HDT at 1.82 MPa – ASTM D648
26%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
1620 MPa
Flexural Modulus – ASTM D790
81 Shore D
Hardness – ASTM D2240
67 MPa
Flexural Strength – ASTM D790
Ultracur3D® EPD 2006 – Material Properties
310 mPas
Viscosity 30 °C – Cone/Plate Rheometer
11 J/m
Notched Izod (Machined), 30 °C – ASTM D256
88 mPas
Viscosity 50 °C – Cone/Plate Rheometer
11 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1.2 g/cm3
Density (printed part) – ASTM D792
0.7 kJ/m2
Charpy notched, 23 °C – ISO 179-1
2370 MPa
E Modulus – ASTM D638
81°C
HDT at 0.45 MPa – ASTM D648
50 MPa
Ultimate Tensile Strength – ASTM D638
61°C
HDT at 1.82 MPa – ASTM D648
10.3%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
2210 MPa
Flexural Modulus – ASTM D790
80 Shore D
Hardness – ASTM D2240
90 MPa
Flexural Strength – ASTM D790
Ultracur3D® EPD 3500 – Material Properties
600 mPas
Viscosity 30 °C – Cone/Plate Rheometer
25 J/m
Notched Izod (Machined), 23 °C – ASTM D256
160 mPas
Viscosity 50 °C – Cone/Plate Rheometer
600 J/m
Unnotched Izod, 23 °C – ASTM D256
1.18 g/cm3
Density (printed part) – ASTM D792
1.5 kJ/m2
Charpy notched, 23 °C – ISO 179-1
2500 MPa
E Modulus – ASTM D638
70°C
HDT at 0.45 MPa – ASTM D648
60 MPa
Ultimate Tensile Strength – ASTM D638
57°C
HDT at 1.82 MPa – ASTM D648
18%
Elongation at Break – ASTM D638
79 Shore D
Hardness – ASTM D2240
2400 MPa
Flexural Modulus – ASTM D790
110 MPa
Flexural Strength – ASTM D790
Magna Draft – Material Properties
3200 MPa
Tensile Modulus – ASTM D638
90 Shore D
Hardness – ASTM D2240
84 MPa
Ultimate Tensile Strength – ASTM D638
75°C
Heat Deflection Temperature – ASTM D648
4.4%
Elongation at break – ASTM D638
970 cPs
Viscosity – At 25°C Brookfield spindle 3
2840 MPa
Flexural Modulus – ASTM D790
1.16 g/cm3
Density
109 MPa
Flexural Strength – ASTM D790
10<T>
Storage
22.6 J/m
Impact Strength Notched Izod – ASTM D256
Passed
Cytotoxicity – ISO 10993-5
Dental Model UV – Material Properties
2800 MPa
Young´s Modulus – ASTM D638
90 Shore D
Hardness – ASTM D2240
70 MPa
Ultimate Tensile Strength – ASTM D638
< 0.3%
Water absorption after 24 hrs – wt%
4%
Elongation at break – ASTM D638
250 cPs
Viscosity – At 25°C Brookfield spindle 3
1700 MPa
Flexural Modulus – ASTM D790
1.10 g/cm3
Density
3.9 kJ/m2
Impact Strength Notched Izod – ISO 180
10<T>
Storage
Mechanical properties based on fully cured material
Colours:
Beige, Grey, White
Rigid DLFR – Material Properties
2848 MPa
Tensile Modulus – ASTM D638
74 µm/(m∙K)
C.T.E (20°C to 60 °C) – ASTM E831
66 MPa
Ultimate Tensile Strength – ASTM D638
112 µm/(m∙K)
C.T.E (60 °C to 120 °C – ASTM E831
3.5%
Elongation at break – ASTM D638
92 Shore D
Hardness – ASTM D2240
3400 MPa
Flexural Modulus – ASTM D790
0.46%
Water Absorption, Short Term (24 hours) – ASTM D570
115 MPa
Flexural Strength – ASTM D790
0.87%
Water Absorption, Medium Term (72 hours) – ASTM D570
19 J/m
Impact Strength Notched Izod – ASTM D256
1.23%
Water Absorption, Long Term (168 hours) – ASTM D570
260°C
Heat Deflection Temperature (@ 0.45 MPa) – ASTM D648
580 cPs
Viscosity – At 25°C Brookfield spindle 3
86°C
Heat Deflection Temperature (@ 1.82 MPa) – ASTM D648
1.21 g/cm3
Liquid Density
UV-0 (2.0-3.0mm)
Flammability – UL 94
1.32 g/cm3
Printed Part Density
10<T>50°C
Storage
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure L2.
Colours:
Black
Rigid UVFR – Material Properties
4170 MPa
Tensile Modulus – ASTM D638
74 µm/(m∙K)
C.T.E (20°C to 60 °C) – ASTM E831
75 MPa
Ultimate Tensile Strength – ASTM D638
112 µm/(m∙K)
C.T.E (60 °C to 120 °C – ASTM E831
2.3%
Elongation at break – ASTM D638
92 Shore D
Hardness – ASTM D2240
3400 MPa
Flexural Modulus – ASTM D790
0.4%
Water Absorption, Short Term (24 hours) – ASTM D570
115 MPa
Flexural Strength – ASTM D790
0.8%
Water Absorption, Medium Term (72 hours) – ASTM D570
22 J/m
Impact Strength Notched Izod – ASTM D256
1.2%
Water Absorption, Long Term (168 hours) – ASTM D570
260°C
Heat Deflection Temperature (@ 0.45 MPa) – ASTM D648
580 cPs
Viscosity – At 25°C Brookfield spindle 3
94°C
Heat Deflection Temperature (@ 1.82 MPa) – ASTM D648
1.2 g/cm3
Liquid Density
UV-0 (2.0-3.0mm) | UV-1 (1.5 mm)
Flammability – UL 94
1.3 g/cm3
Printed Part Density
10<T<50°C
Storage
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure L2.
Colours:
Black
Magna Dental Model – Material Properties
Beige
2750 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
56 MPa
Ultimate Tensile Strength – ASTM D638
0.13%
Water absorption (short term) – ASTM D570
2.7%
Elongation at break – ASTM D638
150 cPs
Viscosity – At 25°C Brookfield spindle 3
2570 MPa
Flexural Modulus – ASTM D790
1.10 g/cm3
Density
84 MPa
Flexural Strength – ASTM D790
10<T>
Storage
19.5 J/m
Impact Strength Notched Izod – ASTM D256
Passed
Cytotoxicity – ISO 10993-5
2.5 kJ/m2
Impact Strength Notched Izod – ISO 180
White
3020 MPa
Tensile Modulus – ASTM D638
3.2 kJ/m2
Impact Strength Notched Izod – ISO 180
63 MPa
Ultimate Tensile Strength – ASTM D638
90 Shore D
Hardness – ASTM D2240
4.3%
Elognation – ASTM D638
95°C
Heat Deflection Temperature – ASTM D648
2200 MPa
Flexural Modulus – ASTM D790
900 cPs
Viscosity – At 25°C Brookfield spindle 3
95 MPa
Flexural Strength – ASTM D790
1.09 g/cm3
Density
22.7 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Storage
Flexible UV160 – Material Properties
66.5 MPa
Tensile Modulus – ASTM D412
1.74%
Water absorption (%)* after 24 hrs – ASTM D570
14.5 MPa
Tensile Strength (Break) – ASTM D412
2.65%
Water absorption (%)* after 72 hrs – ASTM D570
160%
Elongation at break – ASTM D412
4.5%
Water absorption (%)* after 7 days – ASTM D570
54 kN/m
Tear Strength – ASTM 624 Type C
470 cPs
Viscosity – At 25°C Brookfield spindle 3
30%
Rebound Resilience – ASTM D412
1.10 g/cm3
Density
86 Shore A
Hardness – ASTM D2240
10<T>
Storage
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure M+
Colours:
TranslucentHard UV – Material Properties
2060 MPa
Tensile Modulus – ASTM D412
60°C
Heat Deflection Temperature – ASTM D638
35 MPa
Ultimate Tensile Strength – ASTM D638
1.19 g/cm3
Density
4%
Elongation at break – ASTM D638
10<T>
Storage
77 Shore D
Hardness – ASTM D2240
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure M+
Colours:
Black, Grey