High Temp DL401 3D Resin

450,00 excl vat

FREE UK shipping on orders over £100

HighTemp DL401 is a rigid resin designed for moulding applications, possessing both high stiffness and ductility, and capable of withstanding high temperatures. Parts created in DL401 show superior compression behaviour, and resistance to fatigue, temperature, and moisture without bending or deforming. HighTemp DL401 can be used for quick printing applications and can print with an impressive layer thickness of 350 microns.

In stock

450,00
1 - 3 Bottles
382,50 (15% off)
4 - 11 Bottles
336,60 (25% off)
12 - 19 Bottles
302,94 (32% off)
20+ Bottles
x

5Kg

Best Used for:

• Hot fluid and gas manifolds
• Moulds and inserts
• Heat resistant housings and fixtures
• Outdoor applications

Features:

• 270°C Heat deflection temperature 
• Excellent long-lasting performance under heat and stress
• Quick and fast prototyping 350 μm layer
• Simulating the strength and stiffness of glass filled Nylon 6
• Smooth surface finish and ability to print fine details
• Minimal shrinkage. dry surface touch
• Ideal for plastic injection moulding

Compatible Printers:

LC Magna and LC Titan

Properties
Tensile Properties
Tensile Modulus *
Ultimate Tensile Strength *
Elongation at break *

3180 MPa

77 MPa

4.8%

ASTM D638
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength *
Flexural Modulus *

123 MPa

3240 MPa

ASTM D790
ASTM D790
Impact Properties
Impact Strength Notched Izod *

16 J/m

ASTM D256

General Properties
Hardness *

Heat Deflection Temperature*

Water Absorption (Short Term) *

Viscosity
Density
Storage
Colour

92 Shore D

270°C

700 cPs

1.10 g/cm3

10<T<50°C

Translucent

ASTM D2240

ASTM D648 @ 0.45 MPa

At 25°C Brookfield spindle 3

*Mechanical properties stated based on fully cured material.

Properties
Tensile Properties
Tensile Modulus *

3180 MPa

ASTM D638

 

Ultimate Tensile Strength *

77 MPa

ASTM D638

 

Elongation at break *

4.8%

ASTM D638
Flexural Properties
Flexural Strength *

123 MPa

ASTM D790

 

Flexural Modulus *

3240 MPa

ASTM D790
Impact Properties

Impact Strength Notched Izod *

 

16 J/m

ASTM D256

General Properties
Hardness *

92 Shore D

ASTM D2240

 

Water Absorption (Short Term)

0.28%

ASTM D570

 

Viscosity

700 cPs

At 25°C Brookfield spindle 3

 

Density
1.10 g/cm3

 

Storage

10<T<50°C

 

Colour

Translucent

*Mechanical properties stated based on fully cured material.

 