Rigid DL240 Plant-Based 3D Resin

(1 customer review)

£300.00 excl vat

FREE UK shipping on orders over £100

Rigid DL240 Plant-Based is a high-performance rigid 3D printing resin which consists of 50% plant based raw materials, offering a substantial reduction on net CO2 emission compared to conventional resins.

In stock

£300.00
1 - 3 Bottles
£255.00 (15% off)
4 - 11 Bottles
£224.40 (25% off)
12 - 19 Bottles
£201.95 (32% off)
20+ Bottles
x
SKU: MAGDLPBAM05 Categories: , ,

Best Used for:

• Fast and accurate prototyping
• Dental models for aligner manufacturing

USPs:

• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally. 
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production. 
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles

Compatible Printers:

LC Magna & LC Titan (Not suitable for UV 3D printers)

Properties

Rigid DL240 Plant-Based Resin

Tensile Properties

Green

Post-cured*

Method

Tensile Modulus

Tensile Strength (Break)

Tensile Strength (Yield)

Elongation at break

1210 MPa

27 MPa

24.3 MPa

19.2%

2440 MPa

56.6 MPa

64.5 MPa

6.1%

ASTM D638

ASTM D638

ASTM D638

ASTM D638

Flexural Properties

Flexural Strength

Flexural Modulus

108 MPa

2656 MPa

ASTM D790

ASTM D790

Impact Properties

Impact Strength Notched Izod

Impact Strength Notched Izod

12.2 J/m

2.2 J/m

ASTM D256

ISO 180

General Properties

Shore Hardness

HDT (@ 0.455 MPa)

HDT (@ 1.82 MPa)

Water Absorption %* after 24 hrs

Water Absorption %* after 72 hrs

Water Absorption %* after 7 days

88 Shore D

78.4 °C

62.6 °C

0.470%

0.625%

0.933%

ASTM D2240

ASTM D648

ASTM D648

ASTM D570

ASTM D570

ASTM D570

Liquid Properties

Viscosity

Density

Storage

Colour

580 cPs

1.10 g/cm3

10<T>50°C

Translucent

At 25°C Brookfield spindle 3

* Post cured for 2 hours at 60°C with Photocentric Cure L2

Download TDS >       

 

Best Used for:

• Fast and accurate prototyping
• Dental models for aligner manufacturing

USPs:

• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally.
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production.
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles

Compatible Printers:

LC Magna & LC Titan (Not suitable for UV 3D printers)

Properties

Rigid DL240 Plant-Based Resin

Tensile Properties

Tensile Modulus

1210 MPa  |  2440 MPa*

ASTM D638

Tensile Strength (Break)

27 MPa  |  56.6 MPa*

ASTM D638

Tensile Strength (Yield)

24.3 MPa  |  64.5 MPa*

ASTM D638

Elongation at break

19.2%  |  6.1%*

ASTM D638

Flexural Properties

Flexural Strength

108 MPa*

ASTM D790

Flexural Modulus

2656 MPa*

ASTM D790

Impact Properties

Impact Strength Notched Izod

12.2 J/m

ASTM D256

2.2 kJ/m2

ISO 180

General Properties

Shore Hardness

84 Shore D*

ASTM D2240

HDT (@ 0.455 MPa)

78.4°C*

ASTM D648

HDT (@ 1.82 MPa)

62.6°C*

ASTM D648

Water absorption (%)* after 24 hrs

0.470%

ASTM D570

Water absorption (%)* after 72 hrs

0.625%

ASTM D570

Water absorption (%)* after 7 days

0.933%

ASTM D570

Liquid Properties

Viscosity

580 cPs

At 25°C Brookfield spindle 3

Density

1.10 g/cm3

Storage

10<T>50°C

Colour

Dark Amber

* Post cured for 2 hours at 60°C with Photocentric Cure L2