Durable DL902 Plant-Based 3D Resin
$420.00 excl vat
FREE UK shipping on orders over £250
Tough, ABS-like parts from 52% bio-based materials, reducing CO₂ while producing strong parts that flex under pressure.
Best Used for:
DL902 is ideal for printing functional prototypes and end-use parts that require a careful balance of strength, stiffness, and toughness.
Compatible Printers:
LC Magna (Not suitable for UV 3D Printers)
Unique Features:
- Tough and Flexible - Similar to ABS or polypropylene blends
- High Durability – Difficult to break under typical use
- Plant-Based - Made with 52% bio-renewable content
- Low Water Absorption - Printed parts absorb low amounts of water
- Moderate Heat Resistance - No deformation below 73°C
Product Overview
Bicycle Bottle Holder
LC Magna Printing Process
Bicycle Bottle Holder 360
Properties
Tensile Properties
Tensile Modulus *
Tensile Strength (Break)*
Tensile Strength (Yield)*
Elongation at break *
2290 MPa
37 MPa
46 MPa
37%
ASTM D638
ASTM D638
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength *
Flexural Modulus *
71 MPa
1790 MPa
ASTM D790
ASTM D790
Impact Properties
Impact Strength Notched Izod *
51 J/m
ASTM D256
General Properties
Hardness *
Heat Deflection Temperature*
Water Absorption (%) after 24 hrs
Water Absorption (%) after 72 hrs
Water Absorption (%) after 7 days
Viscosity
Density
Storage
Colours
82 Shore D
73°C
0.28%
0.34%
0.53%
900 cPs
1.06 g/cm3
10<T<50°C
Black
ASTM D2240
ASTM D648
ASTM D570
ASTM D570
ASTM D570
Brookfield Spindle 3
*Post cured for 3 hrs at 60°C in Photocentric Cure L2.
Best Used for:
DL902 is ideal for printing functional prototypes and end-use parts that require a careful balance of strength, stiffness, and toughness.
Compatible Printers:
LC Magna (Not suitable for UV 3D Printers)
USPs:
- Tough and Flexible - Similar to ABS or polypropylene blends
- High Durability – Difficult to break under typical use
- Plant-Based - Made with 52% bio-renewable content
- Low Water Absorption - Printed parts absorb low amounts of water
- Moderate Heat Resistance - No deformation below 73°C
Properties
Tensile Properties
Tensile Modulus *
2290 MPa
ASTM D638
Tensile Strength (Break) *
37 MPa
ASTM D638
Tensile Strength (Yield)*
46 MPa
ASTM D638
Elongation at break *
37%
ASTM D638
Flexural Properties
Flexural Strength *
71 MPa
ASTM D790
Flexural Modulus *
1790 MPa
ASTM D790
Impact Properties
Impact Strength Notched Izod *
51 J/m
ASTM D256
General Properties
Hardness *
82 Shore D
ASTM D2240
Heat Deflection Temperature*
73°C
ASTM D648
Water Absorption (%) after 24 hrs
0.28%
ASTM D570
Water absorption (%) after 72 hrs
0.34%
ASTM D570
Water absorption (%) after 7 days
0.53%
ASTM D570
Viscosity
900 cPs
At 25°C Brookfield spindle 3
Density
1.06 g/cm3
Storage
10<T<50°C
Colours
Black
*Post cured for 3 hrs at 60°C in Photocentric Cure L2.
“Bicycle Bottle Cage / Holder” model by PretEnGineering, licensed under Creative Commons (CC-BY-SA-4.0)
https://creativecommons.org/licenses/by/4.0/ - Remix by An2