Deep Blue Transparent Tough Resin – Made for Prusa Research by Photocentric
£50.32 excl vat
FREE UK shipping on orders over £100
New high-quality, tough resin specially made for Prusa Research by Photocentric. This resin was developed by Photocentric using the Original Prusa SL1 for testing. Due to the fact, the SL1 was the main printer throughout the development process. It prints the resin fast while providing top notch print quality. The Resins made for Prusa Research by Photocentric are among the best 405nm tough resins for 3D printing out there.
1Kg
One of the most significant properties is the vibrant color. Bright, rich, and stable over time.
The capability to print the tiniest details is a matter of course. However, with this resin, you will also achieve a very smooth and nice to touch surfaces.
This resin is universal, and you can use it for a number of applications. It is suitable for printing functional or decorative parts. You can really utilize its mechanical properties for printing any spare parts you can’t buy anymore. But it is also great for tabletop gaming accessories, parts for cosplay costumes, and so on.
Compatible Printers:
Prusa SL1S
Not compatible with Liquid Crystal Opus
Printing Setup
Exposure time / layer height 0.05
7/35 seconds
Properties
UV Tough Resin
Tensile Modulus *
Ultimate Tensile Strength *
2100 MPa
55 MPa
5%
Water Absorption (%) after 24h
< 0.2
1.13 g/cm3
* Mechanical properties stated based on fully cured material
Properties
UV Tough Resin
Tensile Modulus *
2100 MPa
Ultimate Tensile Strength*
55 MPa
ASTM D638
Water Absorption (%) after 24 h
< 0.2
1.13 g/cm3
10<T>50°C
* Mechanical properties stated based on fully cured material.
% elongation: How much an object can be stretched from its original shape.
Young’s Modulus: How much force is needed to stretch an object.
Flexural Strength: Ability to resist deformation under load.
Flexural Modulus: Measurement of an objects resistance to bend when force is applied (bend modulus).
HDT: Temperature at which a plastic deforms under heat.