Daylight High Tensile

High Tensile daylight polymers are ideal for making hard objects that exhibit high strength and low elongation. Objects will not bend or deflect easily when under duress. They exhibit very high tensile shear properties, low elongation, and little shrinkage.

Printer Compatibility

Compatible with Liquid Crystal 10″, HR & HR2

Size: 1kg

Technical Data

Colour: White

Viscosity 980 cPs (At 25ºC Brookfield spindle 3)

Hardness 92 Shore D ASTM D2240 (After post exposure)

Tensile strength 81 MPa ASTM D638 (After post exposure Postcured 120 mins UV and heat 60°C water)

Elongation at break 4.8% ASTM D638 (Postcured 120 mins UV and heat 60°C water)

Storage 10<t>50°C

Density 1.09 g/cm3

Processing Instructions

Follow the procedures laid out in your 3D Liquid Crystal user manual. Polymer should be poured into the tray away from direct sunlight. Polymer can be reused but should be poured through a filter to remove solid lumps. Keep hood on at all times. Liquid polymer is soluble in water and soap. Object should be post cured under UV in water to remove any surface tack, followed by UV light at 80 °C for minimum of 1 hour to obtain the maximum tensile properties.