Dental Model UV 3D Resin
£60.00 – £300.00 excl vat
FREE UK shipping on orders over £100
If you are looking for dental resin, Photocentric Dental Model UV photopolymer resin has been formulated to create detailed, high resolution dental models. The dental resin has been developed in conjunction with Dental Technologists to ensure an optimal colour, feel, and working characteristics. Ideal for orthodontic, study and working models. The prints show minimal shrinkage with a tolerance of 50µm max deviation on a full arch. Printed dental parts exhibit extremely high tensile properties and hardness, allowing for their use as a working or a vacuum forming model.
Key Features:
• High Accuracy
• Strong
• Low Shrinkage
Compatible Printers:
LC Opus, LC Dental, Anycubic, Wanhao, Phrozen, Sparkmaker, Kudo Bean, MoonRay, Asiga, Envisontec, Flashforge and more
Properties
Dental Model UV Resin
Tensile Properties
Tensile Strength *
Elongation at break *
70 MPa
4%
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength *
Flexural Modulus *
85 MPa
85 MPa
1700 MPa
ASTM D792
ASTM D792
Impact Properties
Impact Strength Notched Izod *
3.9 kJ/m2
ISO 180
General Properties
Hardness *
Viscosity
Density
Storage
90 Shore D
250 cPs
1.10 g/cm3
10<T>50°C
ASTM D2240
At 25°C Brookfield spindle 3
* Post cured for 2hr at 60°C
Key Features:
• High Accuracy
• Strong
• Low Shrinkage
Compatible Printers:
LC Dental, Anycubic, Wanhao, Phrozen, Sparkmaker, Kudo Bean, MoonRay, Asiga, Envisontec, Flashforge and more
Properties
Dental Model UV Resin
Tensile Properties
Tensile Strength *
70 MPa
ASTM D638
Elongation at break *
4%
ASTM D638
Flexural Properties
Flexural Strength *
85 MPa
ASTM D790
Flexural Modulus *
1700 MPa
ASTM D790
Impact Properties
Impact Strength Notched Izod *
3.9 kJ/m2
ISO 180
General Properties
Hardness *
90 Shore D
ASTM D2240
Viscosity
250 cPs
At 25°C Brookfield spindle 3
Density
1.10 g/cm3
Storage
10<T>50°C
* Post cured for 1hr at 60°C in Cure L2