Photocentric manufacture a range of functional resins for a wide variety of applications.
We are a vertically integrated chemical manufacturer, reacting hundreds of tonnes of polymers through to formulating resins.
Materiali per la stampa 3D
Photocentric manufacture a range of functional resins for a wide variety of applications.
We are a vertically integrated chemical manufacturer, reacting hundreds of tonnes of polymers through to formulating resins.
Durevole DL110H
Impact and compression resistant grade that allows some bending and stress fatigue without breaking or deforming.
Applicazioni
Jigs and fixtures requiring minimal deflection at elevated temperatures, cover plates and enclosures, fastenings, tools and couplings, strong and stiff prototypes, props.
Stampanti compatibili
5kg from
£300.00 IVA esclusa
Volume discounts available
DLFR rigido
Rigid DLFR has UL 94 V-0 certification, even showing self-extinguishing properties in the green state. It exhibits exceptionally high HDT and high tensile modulus.
Applicazioni
Any application requiring durable rigid flame-retardant properties, for instance electrical enclosures and connectors, high power electrical appliances and battery housings.
Stampanti compatibili
5kg from
£252.45 - £375.00 IVA esclusa
Volume discounts available
UVFR rigido
Rigid UVFR has UL 94 V-0 certification, even showing self-extinguishing properties in the green state. It exhibits exceptionally high HDT and high tensile modulus.
Applicazioni
Any application requiring durable rigid flame-retardant properties, for instance electrical enclosures and connectors, high power electrical appliances and battery housings.
Stampanti compatibili
1kg from
£50.49 - £75.00 IVA esclusa
Volume discounts available
Alta temperatura DL401
Rigid, high temperature material possessing high
stiffness and ductility.
Applicazioni
Hot fluid and gas manifolds, moulds and inserts, heat resistant housings and fixtures
Stampanti compatibili
5kg from
£252.45 - £375.00 IVA esclusa
Volume discounts available
Alta temperatura DL400
Extremely high operating temperatures of up to 230°C without bending or deforming, simulating the properties of glass filled Nylon 6.
Applicazioni
Hot fluid and gas manifolds, moulds and inserts, heat resistant housings and fixtures.
Stampanti compatibili
5kg from
£252.45 - £375.00 IVA esclusa
Volume discounts available
Elastic DL160
High energy dampening at room and even low temperatures (-25 °C) with rebound resilience of 10%, 90% of energy is absorbed.
Applicazioni
Sportswear protection and helmets, cold temperature flexibility, dampening rubbers and foams, gaskets and seals
Stampanti compatibili
5kg from
£375.00 IVA esclusa
Volume discounts available
Magna Hard
Very high green strength and low shrinkage make this a reliable grade for printing. Cured parts exhibit extreme hardness with little compression under force.
Applicazioni
Functional end use and prototype parts.
Stampanti compatibili
5kg from
£168.30 - £250.00 IVA esclusa
Volume discounts available
High Tensile UV
Ideal for making objects with a high tensile strength and hardness that cannot be bent or compressed easily..
Applicazioni
Prototyping and functional engineering
Stampanti compatibili
1kg from
£33.66 - £50.00 IVA esclusa
Volume discounts available
Rigido DL240 a base vegetale
Rigid tough material with over 50% plant based raw materials, offering a substantial reduction in embedded Carbon.
Applicazioni
Fast prototyping, accurate parts, dental models for aligner manufacturing.
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
Rigido UV240 a base vegetale
Rigid tough material with over 50% plant based raw materials, offering a substantial reduction in embedded Carbon.
Applicazioni
Fast prototyping, accurate parts, dental models for aligner manufacturing.
Stampanti compatibili
1kg from
£40.39 - £60.00 IVA esclusa
Volume discounts available
Durevole UV80
Tough, functional parts that are durable, long-lasting and have high impact strength.
Applicazioni
Jigs and fixtures, cover plates and enclosures and end-use parts.
Stampanti compatibili
1kg from
£50.49 - £75.00 IVA esclusa
Volume discounts available
Magna Duramax
Functional durable parts with high impact strength.
Applicazioni
Jigs and fixtures requiring minimal deflection, cover plates and enclosures, fastenings, tools and couplings.
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
UV Basics
La prima scelta per una stampa accurata e a basso costo. L'assenza di irritazione e il basso odore rendono la stampa e la post-elaborazione più sicure e semplici.
Applicazioni
End use, fast prototyping and accurate models
Stampanti compatibili
1kg from
£19.99 IVA esclusa
Flessibile DL220B
Combines impact absorption, high elongation, efficient energy damping, good tear strength and very low water absorption
Applicazioni
Sport protection helmets, shock absorption, phone cases, cushioning
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
Ultracur3D® EPD1006
Functional parts capable of movement and flexibility without breaking.
Applicazioni
Functional engineering parts and prototyping
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
Ultracur3D® EPD1086
Multi-purpose grade with balanced mechanical properties.
Applicazioni
Engineering and prototype parts
Stampanti compatibili
5kg from
£168.30 - £250.00 IVA esclusa
Volume discounts available
Ultracur3D® EPD2006
Materiale rigido, resistente e duraturo che garantisce la massima precisione nei dettagli.
Applicazioni
Engineering and prototyping parts requiring resilience with some compression
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
Ultracur3D® EPD3500
Forte resina traslucida diurna con resistenza e rigidità superiori.
Applicazioni
Functional engineering parts and prototyping
Stampanti compatibili
5kg from
£252.45 - £375.00 IVA esclusa
Volume discounts available
Magna Dental Model
Creates highly accurate, high-resolution models ideal for thermoforming orthodontic models for aligner manufacture.
Applicazioni
Orthodontic models
Stampanti compatibili
5kg from
£300.00 IVA esclusa
Volume discounts available
Dental Model UV
Creates highly accurate, high-resolution models ideal for thermoforming orthodontic models for aligner manufacture.
Applicazioni
Orthodontic models
Stampanti compatibili
1kg & 5kg from
£60.00 - £300.00 IVA esclusa
Volume discounts available
Bozza Magna
La nostra resina da stampa più veloce, paragonabile all'acrilico e alle poliammidi.
Applicazioni
Prototipazione rapida
Stampanti compatibili
5kg from
£201.95 - £300.00 IVA esclusa
Volume discounts available
Flexible UV160
Highly elastic stiff 3D resin with an 86A shore hardness suitable for end user functional parts, presenting TPU properties.
Applicazioni
Seals, gaskets, grips and handles, cushioning, footwear
Stampanti compatibili
1kg from
£50.49 - £75.00 IVA esclusa
Volume discounts available
Hard UV
Very high green strength and low shrinkage make this a reliable grade for printing. Cured parts exhibit extreme hardness with little compression under force.
Applicazioni
Functional parts, prototypes, compression-resisting parts
Stampanti compatibili
1kg
£27.50 - £50.00 IVA esclusa
Volume discounts available
Durable UV SuperClear
Ideal for making clear, strong objects with only minimal shrinkage. Durable UV SuperClear has been specifically developed to allow the fabrication of extremely clear objects.
Applicazioni
Clear and durable models, end user parts like push fits, fluidics and microfluidics
Stampanti compatibili
1kg
£40.39 - £60.00 IVA esclusa
Photocentric Pulitore di resina 30
Photocentric Resin Cleaner 30 has been optimally formulated to remove photopolymer resin, rapidly cleaning even the most intricate, detailed parts. It reduces post curing times and leaves parts shiny and dry to touch.
£53.20 - £199.95 IVA esclusa
5L & 20L available
Left part washed with IPA vs right part washed with resin cleaner
DL110H – Material Properties
2100 MPa
Tensile Modulus – ASTM D638
86 Shore D
Hardness – ASTM D2240
54 MPa
Ultimate Tensile Strength – ASTM D638
75°C
Heat Deflection Temperature – ASTM D648
28%
Elongation at break – ASTM D638
0.62%
Water Absorption (Short Term) – 1 x 1 x 1 cm3 cube
1950 MPa
Flexural Modulus – ASTM D790
480 cPs
Viscosity – At 25°C Brookfield spindle 3
78 MPa
Flexural Strength – ASTM D790
1,14 g/cm3
Densità
110 J/m
Impact Strength Notched Izod – ASTM D256
10<T<50°C
Immagazzinamento
Le proprietà meccaniche si basano sul materiale completamente polimerizzato.
Colours:
Nero 
Translucent
High Temp DL401 – Material Properties
3180 MPa
Tensile Modulus – ASTM D638
3.5
Relative Permittivity, 20°C
77 MPa
Ultimate Tensile Strength – ASTM D638
4.05
Relative Permittivity, 100°C
4.8%
Elongation at break – ASTM D638
30 x 10-3
Dielectric Loss Factor, 20°C
3240 MPa
Flexural Modulus – ASTM D790
31 x 10-3
Dielectric Loss Factor, 100°C
123 MPa
Flexural Strength – ASTM D790
92 D
Hardness – ASTM D2240
16 J/m
Impact Strength Notched Izod – ASTM D256
270°C
Heat Deflection Temperature – ASTM D648 (0.45 MPa)
0.20 W/(m.K)
Thermal Conductivity, 23°C – ASTM D7984
0.28 wt%
Water Absorption (Short Term) – ASTM D570
0.21 W/(m.K)
Thermal Conductivity, 100°C – ASTM D7984
700 cPs
Viscosity – At 25°C Brookfield spindle 3
1.36 J/(g.K)
Specific Heat Capacity, 23°C – ASTM D7984
1,1 g/cm3
Densità
1.69 J/(g.K)
Specific Heat Capacity, 100°C – ASTM D7984
10<T<50°C
Immagazzinamento
Mechanical properties stated based on fully cured material. Post cured for 2hrs at 60°C in Cure L2 or Cure XL
Colours:
Translucent Elastic DL160A – Material Properties
13 MPa
Tensile Modulus – ASTM D412
70 Shore A
Hardness – ASTM D2240
12 MPa
Tensile Strength (Break) – ASTM D412
-24 °C
Tg (DSC, S1 –57, S2 8)
2 MPa
Tensile strength @ 50% Elongation – ASTM D412
0.34%
Water absorption (%)* after 24 hrs – ASTM D570
4 MPa
Tensile strength @ 100% Elongation- ASTM D412
0.38%
Water absorption (%)* after 72 hrs – ASTM D570
162%
Elongation at Break – ASTM D412
0.56%
Water absorption (%)* after 7 days – ASTM D570
20 kN/m
Tear Strength – ASTM 624
1100 cPs
Viscosity – At 25°C Brookfield spindle 3
10%
Rebound Resilience – ASTM D7121
1.04 g/cm3
Densità
10<T<
Immagazzinamento
Post cured for 2 hours at 60°C with Photocentric Cure L2
Colours:
Translucent
Elastic DL160B – Material Properties
19,5 MPa
Tensile Modulus – ASTM D412
74 Shore A
Hardness – ASTM D2240
12 MPa
Tensile Strength (Break) – ASTM D412
-24 °C
Tg (DSC, S1 –57, S2 8)
2.5 MPa
Tensile strength @ 50% Elongation – ASTM D412
0.29%
Water absorption (%)* after 24 hrs – ASTM D570
18 MPa
Tensile strength @ 100% Elongation- ASTM D412
0.38%
Water absorption (%)* after 72 hrs – ASTM D570
162%
Elongation at Break – ASTM D412
0.56%
Water absorption (%)* after 7 days – ASTM D570
1100 cPs
Viscosity – At 25°C Brookfield spindle 3
20 kN/m
Tear Strength – ASTM 624
10%
Rebound Resilience – ASTM D7121
1.04 g/cm3
Densità
10<T<
Immagazzinamento
Post cured for 2 hours at 60°C with Photocentric Cure L2
Colours:
NeroSchede tecniche e di sicurezza
Selezionare la resina e la lingua di seguito
Our 3D resins are compliant with REACH, SVHC and RoHS
High Temp DL400 – Material Properties
4000 MPa
Tensile Modulus – ASTM D638
95 Riva D
Hardness – ASTM D2240
80 MPa
Ultimate Tensile Strength – ASTM D638
230°C
Heat Deflection Temperature – ASTM D648 (0.455 MPa)
4%
Elongation at break – ASTM D638
0.35%
Water Absorption (Short Term) – ASTM D570
3300 MPa
Flexural Modulus – ASTM D790
650 cPS
Viscosity – At 25°C Brookfield spindle 3
109 MPa
Flexural Strength – ASTM D790
1,10 g/cm3
Densità
15,8 J/m
Impact Strength Notched Izod – ASTM D256
10<T>50°C
Immagazzinamento
3,1 kJ/m2
Impact Strength Notched Izod – ISO 180
Passato
Cytotoxicity – ISO 10993-5
Le proprietà meccaniche si basano sul materiale completamente polimerizzato.
Colours:
Translucent Magna Hard – Material Properties
2080 MPa
Tensile Modulus – ASTM D638
100 J/m
Impact Strength Notched Izod – ASTM D256
57 MPa
Ultimate Tensile Strength – ASTM D638
86 Shore D
Hardness – ASTM D2240
8%
Elongation at break – ASTM D638
90°C
Heat Deflection Temperature – ASTM D648
1550 MPa
Flexural Modulus- ASTM D790
450 cPs
Viscosity – At 25°C Brookfield spindle 3
65 MPa
Flexural Strength – ASTM D790
1,1 g/cm3
Densità
10<T<
Immagazzinamento
Le proprietà meccaniche si basano sul materiale completamente polimerizzato.
Colours:
NeroHigh Tensile UV – Material Properties
2610 MPa
Tensile Modulus – ASTM D638
80 Shore D
Hardness – ASTM D2240
65 MPa
Ultimate Tensile Strength – ASTM D638
63°C
Heat Deflection Temperature – ASTM D648
6%
Elongation at break – ASTM D638
510 cPs
Viscosity – At 25°C Brookfield spindle 3
1910 MPa
Flexural Modulus- ASTM D790
1,16 g/cm3
Densità
8,1 kJ/m2
Impact Strength Notched Izod – ISO 180
10<T>50°C
Immagazzinamento
Le proprietà meccaniche si basano sul materiale completamente polimerizzato.
Colours:
GrigioRigid DL240 – Material Properties
2440 MPa
Tensile Modulus – ASTM D638
88 Shore D
Hardness – ASTM D2240
56,6 MPa
Tensile Strength (Break) – ASTM D638
78.4°C
HDT (@ 0.455 MPa) – ASTM D648
64,5 MPa
Tensile Strength (Yield) – ASTM D638
62.6°C
HDT (@ 1.82 MPa) – ASTM D648
6.1%
Elongation at Break – ASTM D638
0.470%
Water absorption (%)* after 24 hrs – ASTM D570
108 MPa
Flexural Strength – ASTM D790
0.625%
Water absorption (%)* after 72 hrs – ASTM D570
2656
Flexural Modulus – ASTM D790
0.933%
Water absorption (%)* after 7 days – ASTM D570
12,2 J/m
Impact Strength Notched Izod – ASTM 256
580 cPs
Viscosity – At 25°C Brookfield spindle 3
2,2 kJ/m2
Impact Strength Notched Izod – ISO 180
1,10 g/cm3
Densità
10<T>50°C
Immagazzinamento
Mechanical properties based on post curing for 2 hours at 60°C with Photocentric Cure L2
Colours:
Translucent
Rigid UV240 – Material Properties
2080 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
52 MPa
Tensile Strength (Break) – ASTM D638
78.4°C
HDT (@ 0.455 MPa) – ASTM D648
54 MPa
Tensile Strength (Yield) – ASTM D638
62.6°C
HDT (@ 1.82 MPa) – ASTM D648
5.4%
Elongation at Break – ASTM D638
0.470%
Water absorption (%)* after 24 hrs – ASTM D570
108 MPa
Flexural Strength – ASTM D790
0.625%
Water absorption (%)* after 72 hrs – ASTM D570
2656
Flexural Modulus – ASTM D790
0.933%
Water absorption (%)* after 7 days – ASTM D570
12,2 J/m
Impact Strength Notched Izod – ASTM 256
580 cPs
Viscosity – At 25°C Brookfield spindle 3
2,2 kJ/m2
Impact Strength Notched Izod – ISO 180
1,10 g/cm3
Densità
10<T>50°C
Immagazzinamento
Mechanical properties based on post curing for 2 hours at 60°C with Photocentric Cure M+
Colours:
Translucent Durable UV80 – Material Properties
1940 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
46 MPa
Ultimate Tensile Strength – ASTM D638
65°C
Heat Deflection Temperature
13%
Elongation at break – ASTM D638
400 cPs
Viscosity – At 25°C Brookfield spindle 3
28 MPa
Flexural Strength – ASTM D790
1,10 g/cm3
Densità
760 MPa
Flexural Modulus – ASTM D790
10<T>
Immagazzinamento
8,1 kJ/m2
Impact Strength Notched Izod – ISO 180
Magna Duramax – Material Properties
1760 MPa
Tensile Modulus – ASTM D638
70 Riva D
Hardness – ASTM D2240
50 MPa
Ultimate Tensile Strength – ASTM D638
60°C
Heat Deflection Temperature – ASTM D648
19%
Elongation at break – ASTM D638
1.4%
Water Absorption (Short Term) – ASTM D570
1600 MPa
Flexural Modulus – ASTM D790
395 cPs
Viscosity – At 25°C Brookfield spindle 3
70 MPa
Flexural Strength – ASTM D790
1,11 g/cm3
Densità
51 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Immagazzinamento
5,4 kJ/m2
Impact Strength Notched Izod – ISO 180
UV Basics – Material Properties
2330 MPa
Tensile Modulus – ASTM D638
110°C
Heat Deflection Temperature – ASTM D648
57,8 MPa
Ultimate Tensile Strength – ASTM D638
0.1%
Assorbimento d'acqua (%) dopo 24 ore
6%
Elongation at break – ASTM D638
1.4%
Assorbimento d'acqua (%) dopo 72 ore
2190 MPa
Flexural Modulus – ASTM D790
0.6%
Assorbimento d'acqua (%) dopo 7 giorni
86,6 MPa
Flexural Strength – ASTM D790
740 cPs
Viscosity – At 25°C Brookfield spindle 3
42.4 J/m
Impact Strength Notched Izod – ASTM D256
1,10 g/cm3
Densità
87 Shore D
Hardness – ASTM D2240
10<T>
Immagazzinamento
Flexible DL220B – Material Properties
66,4 MPa
Tensile Modulus – ASTM D412
0.32%
Water absorption (%) after 24 hrs – ASTM D570
14 MPa
Tensile Strength (Break) – ASTM D412
0.53%
Water absorption (%) after 72 hrs – ASTM D570
211%
Elongation at break – ASTM D412
1.09%
Water absorption (%)* after 7 days – ASTM D570
21 kN/m
Tear Strength – ASTM 624 Type C
1600 cPs
Viscosity – At 25°C Brookfield spindle 3
19.6%
Rebound Resilience – ASTM D7121
1,06 g/cm3
Densità
42.4 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Immagazzinamento
80 Shore A
Hardness – ASTM D2240
Ultracur3D® EPD 1006 – Material Properties
1033 mPas
Viscosity 30 °C – Cone/Plate Rheometer
20 J/m
Notched Izod (Machined), -30 °C – ASTM D256
268 mPas
Viscosity 50 °C – Cone/Plate Rheometer
35 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1.2 g/cm3
Density (printed part) – ASTM D792
2.5 kJ/m2
Charpy notched, 23 °C – ISO 179-1
1500 MPa
E Modulus – ASTM D638
44°C
HDT at 0.45 MPa – ASTM D648
40 MPa
Ultimate Tensile Strength – ASTM D638
40°C
HDT at 1.82 MPa – ASTM D648
25%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
1460 MPa
Flexural Modulus – ASTM D790
0.83 %
Water Absorption, Short Term (24 hours) – ASTM D570
52 MPa
Flexural Strength – ASTM D790
79 Shore D
Hardness – ASTM D2240
Ultracur3D® EPD 1086 – Material Properties
450 mPas
Viscosity 30 °C – Cone/Plate Rheometer
28 J/m
Notched Izod (Machined), 23 °C – ASTM D256
130 mPas
Viscosity 50 °C – Cone/Plate Rheometer
606 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1,18 g/cm3
Density (printed part) – ASTM D792
2.6 kJ/m2
Charpy notched, 23 °C – ISO 179-1
1810 MPa
E Modulus – ASTM D638
53°C
HDT at 0.45 MPa – ASTM D648
42 MPa
Ultimate Tensile Strength – ASTM D638
46°C
HDT at 1.82 MPa – ASTM D648
26%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
1620 MPa
Flexural Modulus – ASTM D790
81 Shore D
Hardness – ASTM D2240
67 MPa
Flexural Strength – ASTM D790
Ultracur3D® EPD 2006 – Material Properties
310 mPas
Viscosity 30 °C – Cone/Plate Rheometer
11 J/m
Notched Izod (Machined), 30 °C – ASTM D256
88 mPas
Viscosity 50 °C – Cone/Plate Rheometer
11 J/m
Notched Izod (Machined), 23 °C – ASTM D256
1.2 g/cm3
Density (printed part) – ASTM D792
0.7 kJ/m2
Charpy notched, 23 °C – ISO 179-1
2370 MPa
E Modulus – ASTM D638
81°C
HDT at 0.45 MPa – ASTM D648
50 MPa
Ultimate Tensile Strength – ASTM D638
61°C
HDT at 1.82 MPa – ASTM D648
10.3%
Elongation at Break – ASTM D638
HB
Flammability – UL 94 1.5 mm
2210 MPa
Flexural Modulus – ASTM D790
80 Shore D
Hardness – ASTM D2240
90 MPa
Flexural Strength – ASTM D790
Ultracur3D® EPD 3500 – Material Properties
600 mPas
Viscosity 30 °C – Cone/Plate Rheometer
25 J/m
Notched Izod (Machined), 23 °C – ASTM D256
160 mPas
Viscosity 50 °C – Cone/Plate Rheometer
600 J/m
Unnotched Izod, 23 °C – ASTM D256
1,18 g/cm3
Density (printed part) – ASTM D792
1.5 kJ/m2
Charpy notched, 23 °C – ISO 179-1
2500 MPa
E Modulus – ASTM D638
70°C
HDT at 0.45 MPa – ASTM D648
60 MPa
Ultimate Tensile Strength – ASTM D638
57°C
HDT at 1.82 MPa – ASTM D648
18%
Elongation at Break – ASTM D638
79 Shore D
Hardness – ASTM D2240
2400 MPa
Flexural Modulus – ASTM D790
110 MPa
Flexural Strength – ASTM D790
Magna Draft – Material Properties
3200 MPa
Tensile Modulus – ASTM D638
90 Shore D
Hardness – ASTM D2240
84 MPa
Ultimate Tensile Strength – ASTM D638
75°C
Heat Deflection Temperature – ASTM D648
4.4%
Elongation at break – ASTM D638
970 cPs
Viscosity – At 25°C Brookfield spindle 3
2840 MPa
Flexural Modulus – ASTM D790
1,16 g/cm3
Densità
109 MPa
Flexural Strength – ASTM D790
10<T>
Immagazzinamento
22,6 J/m
Impact Strength Notched Izod – ASTM D256
Passato
Cytotoxicity – ISO 10993-5
Dental Model UV – Material Properties
2800 MPa
Young´s Modulus – ASTM D638
90 Shore D
Hardness – ASTM D2240
70 MPa
Ultimate Tensile Strength – ASTM D638
< 0.3%
Water absorption after 24 hrs – wt%
4%
Elongation at break – ASTM D638
250 cPs
Viscosity – At 25°C Brookfield spindle 3
1700 MPa
Flexural Modulus – ASTM D790
1,10 g/cm3
Densità
3,9 kJ/m2
Impact Strength Notched Izod – ISO 180
10<T>
Immagazzinamento
Mechanical properties based on fully cured material
Colours:
Beige, Grey, White
Rigid DLFR – Material Properties
2848 MPa
Tensile Modulus – ASTM D638
74 µm/(m∙K)
C.T.E (20°C to 60 °C) – ASTM E831
66 MPa
Ultimate Tensile Strength – ASTM D638
112 µm/(m∙K)
C.T.E (60 °C to 120 °C – ASTM E831
3.5%
Elongation at break – ASTM D638
92 Riva D
Hardness – ASTM D2240
3400 MPa
Flexural Modulus – ASTM D790
0.46%
Water Absorption, Short Term (24 hours) – ASTM D570
115 MPa
Flexural Strength – ASTM D790
0.87%
Water Absorption, Medium Term (72 hours) – ASTM D570
19 J/m
Impact Strength Notched Izod – ASTM D256
1.23%
Water Absorption, Long Term (168 hours) – ASTM D570
260°C
Heat Deflection Temperature (@ 0.45 MPa) – ASTM D648
580 cPs
Viscosity – At 25°C Brookfield spindle 3
86°C
Heat Deflection Temperature (@ 1.82 MPa) – ASTM D648
1.21 g/cm3
Liquid Density
UV-0 (2.0-3.0mm)
Flammability – UL 94
1.32 g/cm3
Printed Part Density
10<T>50°C
Immagazzinamento
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure L2.
Colours:
Nero
Rigid UVFR – Material Properties
4170 MPa
Tensile Modulus – ASTM D638
74 µm/(m∙K)
C.T.E (20°C to 60 °C) – ASTM E831
75 MPa
Ultimate Tensile Strength – ASTM D638
112 µm/(m∙K)
C.T.E (60 °C to 120 °C – ASTM E831
2.3%
Elongation at break – ASTM D638
92 Riva D
Hardness – ASTM D2240
3400 MPa
Flexural Modulus – ASTM D790
0.4%
Water Absorption, Short Term (24 hours) – ASTM D570
115 MPa
Flexural Strength – ASTM D790
0.8%
Water Absorption, Medium Term (72 hours) – ASTM D570
22 J/m
Impact Strength Notched Izod – ASTM D256
1.2%
Water Absorption, Long Term (168 hours) – ASTM D570
260°C
Heat Deflection Temperature (@ 0.45 MPa) – ASTM D648
580 cPs
Viscosity – At 25°C Brookfield spindle 3
94°C
Heat Deflection Temperature (@ 1.82 MPa) – ASTM D648
1.2 g/cm3
Liquid Density
UV-0 (2.0-3.0mm) | UV-1 (1.5 mm)
Flammability – UL 94
1.3 g/cm3
Printed Part Density
10<T<50°C
Immagazzinamento
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure L2.
Colours:
Nero
Magna Dental Model – Material Properties
Beige
2750 MPa
Tensile Modulus – ASTM D638
84 Shore D
Hardness – ASTM D2240
56 MPa
Ultimate Tensile Strength – ASTM D638
0.13%
Water absorption (short term) – ASTM D570
2.7%
Elongation at break – ASTM D638
150 cPs
Viscosity – At 25°C Brookfield spindle 3
2570 MPa
Flexural Modulus – ASTM D790
1,10 g/cm3
Densità
84 MPa
Flexural Strength – ASTM D790
10<T>
Immagazzinamento
19.5 J/m
Impact Strength Notched Izod – ASTM D256
Passato
Cytotoxicity – ISO 10993-5
2.5 kJ/m2
Impact Strength Notched Izod – ISO 180
Bianco
3020 MPa
Tensile Modulus – ASTM D638
3.2 kJ/m2
Impact Strength Notched Izod – ISO 180
63 MPa
Ultimate Tensile Strength – ASTM D638
90 Shore D
Hardness – ASTM D2240
4.3%
Elognation – ASTM D638
95°C
Heat Deflection Temperature – ASTM D648
2200 MPa
Flexural Modulus – ASTM D790
900 cPs
Viscosity – At 25°C Brookfield spindle 3
95 MPa
Flexural Strength – ASTM D790
1,09 g/cm3
Densità
22,7 J/m
Impact Strength Notched Izod – ASTM D256
10<T>
Immagazzinamento
Flexible UV160 – Material Properties
66,5 MPa
Tensile Modulus – ASTM D412
1.74%
Water absorption (%)* after 24 hrs – ASTM D570
14,5 MPa
Tensile Strength (Break) – ASTM D412
2.65%
Water absorption (%)* after 72 hrs – ASTM D570
160%
Elongation at break – ASTM D412
4.5%
Water absorption (%)* after 7 days – ASTM D570
54 kN/m
Tear Strength – ASTM 624 Type C
470 cPs
Viscosity – At 25°C Brookfield spindle 3
30%
Rebound Resilience – ASTM D412
1,10 g/cm3
Densità
86 Shore A
Hardness – ASTM D2240
10<T>
Immagazzinamento
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure M+
Colours:
Translucent Hard UV – Material Properties
2060 MPa
Tensile Modulus – ASTM D412
60°C
Heat Deflection Temperature – ASTM D638
35 MPa
Ultimate Tensile Strength – ASTM D638
1,19 g/cm3
Densità
4%
Elongation at break – ASTM D638
10<T>
Immagazzinamento
77 Riva D
Hardness – ASTM D2240
Mechanical properties stated based on post curing for 2 hrs at 60 °C in Photocentric Cure M+
Colours:
Black, Grey
2270 MPa
Tensile Modulus – ASTM D638
85 Riva D
Hardness – ASTM D2240
45 MPa
Tensile Strength (Break) – ASTM D638
71°C
Heat Deflection Temperature – ASTM D648
46 MPa
Tensile Strength (Yield)- ASTM D638
0.33%
Water Absorption (Short Term 24 hrs)
62 MPa
Flexural Strength – ASTM D790
662 cPs
Viscosity – At 25°C Brookfield spindle 3
1730 MPa
Flexural Modulus – ASTM D790
1,10 g/cm3
Densità
90 J/m
Impact Strength Notched Izod – ASTM D256
10<T<50°C
Immagazzinamento
Le proprietà meccaniche si basano sul materiale completamente polimerizzato.
Colours:
Libero