Rigid DL240 Plant-Based 3D Resin

(1 customer review)

£300.00 excl vat

FREE UK shipping on orders over £100

Rigid DL240 Plant-Based is a high-performance rigid 3D printing resin which consists of 50% plant based raw materials, offering a substantial reduction on net CO2 emission compared to conventional resins.

Available on back-order

£300.00
1 - 3 Bottles
£255.00 (15% off)
4 - 11 Bottles
£224.40 (25% off)
12 - 19 Bottles
£201.95 (32% off)
20+ Bottles
x
Best Used for:

• Fast and accurate prototyping
• Dental models for aligner manufacturing

USPs:

• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally.
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production.
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles

Compatible Printers:

LC Magna & LC Titan (Not suitable for UV 3D printers)

Properties
Rigid DL240 Plant-Based Resin
Tensile Properties
Green
Post-cured*
Method
Tensile Modulus
Tensile Strength (Break)
Tensile Strength (Yield)
Elongation at break
1210 MPa
27 MPa
24.3 MPa
19.2%
2440 MPa
56.6 MPa
64.5 MPa
6.1%
ASTM D638
ASTM D638
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength
Flexural Modulus
108 MPa
2656 MPa
ASTM D790
ASTM D790
Impact Properties
Impact Strength Notched Izod
Impact Strength Notched Izod
12.2 J/m
2.2 J/m
ASTM D256
ISO 180
General Properties
Shore Hardness
HDT (@ 0.455 MPa)
HDT (@ 1.82 MPa)
Water Absorption %* after 24 hrs
Water Absorption %* after 72 hrs
Water Absorption %* after 7 days
88 Shore D
78.4 °C
62.6 °C
0.470%
0.625%
0.933%
ASTM D2240
ASTM D648
ASTM D648
ASTM D570
ASTM D570
ASTM D570
Liquid Properties
Viscosity
Density
Storage
Colour
580 cPs
1.10 g/cm3
10<T>50°C
Translucent
At 25°C Brookfield spindle 3
* Post cured for 2 hours at 60°C with Photocentric Cure L2
Best Used for:

• Fast and accurate prototyping
• Dental models for aligner manufacturing

USPs:

• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally.
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production.
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles

Compatible Printers:

LC Magna & LC Titan (Not suitable for UV 3D printers)

Properties
Rigid DL240 Plant-Based Resin
Tensile Properties
Tensile Modulus
1210 MPa  |  2440 MPa*
ASTM D638

 

Tensile Strength (Break)
27 MPa  |  56.6 MPa*
ASTM D638

 

Tensile Strength (Yield)
24.3 MPa  |  64.5 MPa*
ASTM D638

 

Elongation at break
19.2%  |  6.1%*
ASTM D638
Flexural Properties
Flexural Strength
108 MPa*
ASTM D790

 

Flexural Modulus
2656 MPa*
ASTM D790
Impact Properties
Impact Strength Notched Izod
12.2 J/m
ASTM D256

 

2.2 kJ/m2
ISO 180
General Properties
Shore Hardness
84 Shore D*
ASTM D2240

 

HDT (@ 0.455 MPa)
78.4°C*
ASTM D648

 

HDT (@ 1.82 MPa)
62.6°C*
ASTM D648
Water absorption (%)* after 24 hrs
0.470%
ASTM D570
Water absorption (%)* after 72 hrs
0.625%
ASTM D570
Water absorption (%)* after 7 days
0.933%
ASTM D570
Liquid Properties
Viscosity
580 cPs
At 25°C Brookfield spindle 3
Density
1.10 g/cm3
Storage
10<T>50°C
Colour
Dark Amber
* Post cured for 2 hours at 60°C with Photocentric Cure L2

 