Cast DL60 3D Resin
$506.00 excl vat
FREE UK shipping on orders over £250
High-accuracy, low ash, antimony-free patterns delivering clean, even burnout and reliable investment casting results.
5Kg
Best Used for:
Suitable for both shell casting and flask casting
• Shell casting - For medium to large, complex patterns without the need for tooling
• Flask casting - For small to medium, complex patterns, including latticed geometries
• Casting of all common metals - Broad compatibility enabled by its low burnout temperature
Features:
• Wax-free formulation - better dimensional stability and processing.
• Clean burnout - ultra-low ash content ensuring contamination free castings.
• Antimony-free - No trace metals
• Low thermal expansion - minimising risk of shell cracking during burnout.
• Low viscosity - enabling easier processing, printing and fast drainage.
• High green strength - self supporting parts that retain dimensional stability.
• Moisture and humidity resistance - consistent results in demanding environments.
LC Magna and LC Titan
2200 MPa
40 MPa
40%
1880 MPa
76 MPa
50 J/m
Coefficient of Linear Thermal Expansion (20°C - 120°C) *
Coefficient of Linear Thermal Expansion (120°C - 200°C)*
Ash Residue*
Antimony content
Water Absorption 24 hrs
Water Absorption 48 hrs
Water Absorption 7 days
85 Shore D
61°C
66μm/m/°C
-
180μm/m/°C
-
0.1%
0%
0.22%
0.24%
0.43%
630 cPs
1.06g/cm3
0<T<50°C
Black
Internal
-
Internal
-
Internal
-
Internal
Internal
Internal
At 25°C Brookfield spindle 3
Internal
-
*Post cured for 5 hrs at 40°C in Photocentric Cure L2/Cure XL.
2200 MPa
40 MPa
40%
1880 MPa
76 MPa
50 J/m
85 Shore D
HDT (@ 0.455 MPa)
61°C
ASTM D648
Coefficient of Linear Thermal Expansion (20°C - 120°C)
66μm/m/°C
Coefficient of Linear Thermal Expansion (120°C - 200°C)
180μm/m/°C
Ash Residue
0.1%
Antimony content
0.1%
Water Absorption after 24 hrs
0.22%
Water Absorption after 48 hrs
0.24%
Water Absorption after 7 days
0.43%
1.06 g/cm3
Black
*Post cured for 5 hrs at 40°C in Photocentric Cure L2/Cure XL.
Cast DL60 3D Resin
$506.00 excl vat
FREE UK shipping on orders over £250
High-accuracy, low ash, antimony-free patterns delivering clean, even burnout and reliable investment casting results.
5Kg
Best Used for:
Suitable for both shell casting and flask casting
• Shell casting - For medium to large, complex patterns without the need for tooling
• Flask casting - For small to medium, complex patterns, including latticed geometries
• Casting of all common metals - Broad compatibility enabled by its low burnout temperature
Features:
• Wax-free formulation - better dimensional stability and processing.
• Clean burnout - ultra-low ash content ensuring contamination free castings.
• Antimony-free - No trace metals
• Low thermal expansion - minimising risk of shell cracking during burnout.
• Low viscosity - enabling easier processing, printing and fast drainage.
• High green strength - self supporting parts that retain dimensional stability.
• Moisture and humidity resistance - consistent results in demanding environments.
LC Magna and LC Titan
2200 MPa
40 MPa
40%
1880 MPa
76 MPa
50 J/m
Coefficient of Linear Thermal Expansion (20°C - 120°C) *
Coefficient of Linear Thermal Expansion (120°C - 200°C)*
Ash Residue*
Antimony content
Water Absorption 24 hrs
Water Absorption 48 hrs
Water Absorption 7 days
85 Shore D
61°C
66μm/m/°C
-
180μm/m/°C
-
0.1%
0%
0.22%
0.24%
0.43%
630 cPs
1.06g/cm3
0<T<50°C
Black
Internal
-
Internal
-
Internal
-
Internal
Internal
Internal
At 25°C Brookfield spindle 3
Internal
-
*Post cured for 5 hrs at 40°C in Photocentric Cure L2/Cure XL.
2200 MPa
40 MPa
40%
1880 MPa
76 MPa
50 J/m
85 Shore D
HDT (@ 0.455 MPa)
61°C
ASTM D648
Coefficient of Linear Thermal Expansion (20°C - 120°C)
66μm/m/°C
Coefficient of Linear Thermal Expansion (120°C - 200°C)
180μm/m/°C
Ash Residue
0.1%
Antimony content
0.1%
Water Absorption after 24 hrs
0.22%
Water Absorption after 48 hrs
0.24%
Water Absorption after 7 days
0.43%
1.06 g/cm3
Black
*Post cured for 5 hrs at 40°C in Photocentric Cure L2/Cure XL.