Daylight Dental Model 3D Resin
Original price was: £65.00.£32.50Current price is: £32.50. excl vat
Accurate, high resolution models especially for dental work can be created using Dental Model resin. Ideal for Orthodontic, study, and working models and created in collaboration with Dental Technologists to ensure optimal colour, feel and working characteristics.
Key Features:
- High Tensile strength and hardness
- Minimal shrinkage
- Ideal for thermoforming models
Industry:
Dental
Compatible Printers:
LC Precision, LC Precision 1.5, LC HR2, LC HR, LC 10″
(Not suitable for UV 3D printers)
1Kg
Properties
Tensile Properties
Tensile Strength *
Elongation at break *
63 MPa
4.3%
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength *
Flexural Modulus *
93 MPa
2200 MPa
ASTM D792
ASTM D792
Impact Properties
Impact Strength Notched Izod *
3.0 kJ/m2
ISO 180
General Properties
Hardness *
Heat Deflection Temperature *
Viscosity
Density
Storage
90 Shore D
90 °C
900 cPs
1.09 g/cm3
10<T>50°C
ASTM D2240
ASTM D648 (0.455 MPa)
At 25°C Brookfield spindle 3
* Post cured for 2hr at 60°C
Properties
Tensile Properties
Tensile Strength *
63 MPa
ASTM D638
Elongation at break *
4.3%
ASTM D638
Flexural Properties
Flexural Strength *
93 MPa
ASTM D790
Flexural Modulus *
2200 MPa
ASTM D790
Impact Properties
Impact Strength Notched Izod *
3.0 kJ/m2
ISO 180
General Properties
Hardness *
90 Shore D
ASTM D2240
Heat Deflection Temperature *
95 °C
ASTM D648 (0.455 MPa)
Viscosity
900 cPs
At 25°C Brookfield spindle 3
Density
1.09 g/cm3
Storage
10<T>50°C
* Post cured for 1hr at 60°C
Glossary of Key Terms
Tensile strength: Ability for an object to withstand pulling (tensile) force. Measured in units of force per cross-sectional area.
% elongation: How much an object can be stretched from its original shape.
Young’s Modulus: How much force is needed to stretch an object.
Flexural Strength: Ability to resist deformation under load.
Flexural Modulus: Measurement of an objects resistance to bend when force is applied (bend modulus).
HDT: Temperature at which a plastic deforms under heat.