Flexible DL220 3D Resin

£300.00 excl vat

FREE UK shipping on orders over £100

Daylight Flexible Resin- ‘Flexible DL220B’ is an optimised solution for applications which require a combination of impact absorption, high elongation, efficient energy damping, good tear strength and exceptionally low water absorption.

Only 3 left in stock

£300.00
1 - 3 Bottles
£255.00 (15% off)
4 - 11 Bottles
£224.40 (25% off)
12 - 19 Bottles
£201.95 (32% off)
20+ Bottles
x

5Kg

SKU: MAGFLBK05 Categories: , , , , Tag:
Best Used for:

• Sport protection, e.g., shin pads
• Shock and impact absorption, e.g., phone cases
• Cushioning
• Vibration damping, e.g., industrial machinery feet

USPs:

• Remarkable elongation at break >200%
• Slow rebound and efficient energy damping
• Exceptionally low water absorption (<1% after 7 days)
• High definition and resolution
• Easy to print due to its high green strength

Compatible Printers:

LC Magna (Not suitable for UV 3D printers)

Properties

Flexible DL220B Resin

Tensile Properties
Green
Post-cured*
Method
Tensile Modulus
Tensile Strength (Break)
Elongation at break
20 MPa
27 MPa
107%
66.4 MPa
14 MPa
211%
ASTM D412
ASTM D412
ASTM D412
Mechanical Properties
Tear Strength
Rebound Resilience
–
–
21 kN/m
19.6%
ASTM 624 Type C
ASTM D7121
General Properties
Shore Hardness
Water Absorption %* after 24 hrs
Water Absorption %* after 72 hrs
Water Absorption %* after 7 days
–
–
–
–
80 Shore A
0.32%
0.53%
1.09%
ASTM D2240
ASTM D570
ASTM D570
ASTM D570
Liquid Properties
Viscosity
Density
Storage
Colour
–
–
–
1600 cPs
1.06 g/cm3
10<T>50°C

Black

At 25°C Brookfield spindle 3
* Post cured for 10 hours at 60°C with Photocentric Cure L2

Download TDS > 

 

Best Used for:

• Sport protection, e.g., shin pads
• Shock and impact absorption, e.g., phone cases
• Cushioning
• Vibration damping, e.g., industrial machinery feet

USPs:

• Remarkable elongation at break >200%
• Slow rebound and efficient energy damping
• Exceptionally low water absorption (<1% after 7 days)
• High definition and resolution
• Easy to print due to its high green strength

Compatible Printers:

LC Magna (Not suitable for UV 3D printers)

Properties
Flexible DL220B Resin
Tensile Properties
Tensile Modulus
20 MPa  |  66.4 MPa*
ASTM D412

 

Tensile Strength (Break)
2.6 MPa  |  14 MPa*
ASTM D412

 

Elongation at break
107%  |  211%*
ASTM D412
Mechanical Properties
Tear Strength
21 kN/m
ASTM 624 Type C

 

Rebound Resilience
19.6%
ASTM D7121
General Properties
Shore Hardness
80 Shore A*
ASTM D2240

 

Water absorption (%)* after 24 hrs
0.32%
ASTM D570
Water absorption (%)* after 72 hrs
0.53%
ASTM D570
Water absorption (%)* after 7 days
1.09%
ASTM D570
Liquid Properties
Viscosity
1600 cPs
At 25°C Brookfield spindle 3
Density
1.06 g/cm3

 

Storage
10<T>50°C
Colour

Black

* Post cured for 10 hours at 60°C with Photocentric Cure L2

 

Download TDS >

 