UV Laser Hard

Available Colours

White, Clear, Black, Grey

Glass-like prints with a crisp finish are obtained when using our Hard 3D Resin. Prints will retain their shape under stretch and compression whilst displaying a high stiffness and high hardness. When using our Hard Resin you’ll 3D print objects that behave like commercial ABS.  

Price 

£55

$77

Available in 1kg bottles with non-drip cap. 

*Local Tax may apply

 

UV-Black-Skull-Hard

Viscosity
(At 25ºC Brookfield spindle 3)

230 cPs

Hardness 
(ASTM D2240 After post exposure)

77 Shore D

Tensile strength 
(ASTM D638 After Post Exposure)

35 MPa

Tensile strength 
(ASTM D638 Before Post Exposure)

15 MPa

Tensile modulus
(ASTM D638 After Post Exposure)

2060 MPa

Elongation at break 
(ASTM D638 After Post Exposure)

4%

Heat deflection temp
ASTM D648 

60°C

Storage 

10<t>50°C

Density

1.19 g/cm3

Firm-Resin-Icon

UV Laser Firm

Available Colours

Clear, Grey, Black

Need some resin to make you items feel more realistic? Our Firm Resin is the way to go. Ideal for creating parts that hold their shape whilst also being able to bend and flex slightly without snapping. This resin produces parts with similar mechanical behaviour to that of Polypropylene.

Price 

£55

$77

Available in 1kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

560 cPs

Hardness 
(ASTM D2240 After post exposure)

65 Shore D

Tensile strength 
(ASTM D638 After post exposure)

26 MPa

Tensile strength 
(ASTM D638 Before post exposure)

10 MPa

Tensile modulus
(ASTM D638 After post exposure)

700 MPa

Heat deflection temp

52ºC

Elongation at break 
(ASTM D638)

10%

Storage 

10<t>50°C

Density

1.18 g/cm3

Photocentric Flexible Resin Icon

UV Laser Flexible

Available Colours

Clear, Black

Soft, flexible parts can be created using our flexible resin. The 3D printed objects can be stretched without snapping or breaking, making this resin ideal for flexible applications. Thin or hollow structures can be bent or squashed and return to their original shape with ease.

Price 

£55

$77

Available in 1kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

200 cPs

Hardness 
(After post exposure)

85 Shore A

Tensile strength 
ASTM D638 (After post exposure)

4.9 MPa

Tensile strength 
ASTM D638 (Before post exposure)

1.5 MPa

Elongation at break 
(ASTM D638 After Post Exposure)

60%

Storage 

10<t>50°C

Density 

1.18 g/cm3

High-Tensile-Resin-Icon

UV Laser High Tensile

Available Colours

Black

When strong parts are required, our  unique High Tensile is the resin of choice. Capable of producing incredibly detailed parts along with great strength, higher than that of injection moulded Polycarbonate with similar mechanical behaviour. Our 3D High Tensile Resin enables you to 3D print extremely strong and durable parts while maintaining an incredibly high accuracy.

Price 

£55

$77

Available in 1kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

980 cPs

Hardness 
(ASTM D2240 After post exposure)

94 Shore D

Tensile strength 
ASTM D638 (Postcured 120 mins UV and 80°C heat)

80 MPa

Elongation at break 
(ASTM D638 Postcured 120 mins UV and 80°C heat)

5.6%

Storage 

10<t>50°C

Density

1.09 g/cm3

Castable-Resin-Icon_

UV Laser Castable

Available Colours

Pink

Castable resin is great for creating parts to be used for investment casting without the need for laborious wax carving. Each print will have a matte surface to help you visualise how the end casted part will be. It has been designed to burn evenly at regularly increasing temperatures stages to reduce gas pressure in the cast.

Price 

£58

$81

Available in 1kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

230 cPs

Hardness 
(After post exposure)

75 Shore D

Tensile strength 
ASTM D638 (After Post Exposure)

10 MPa

Tensile strength 
ASTM D638 (Before Post Exposure)

6 MPa

Tensile Modulus
ASTM D638 (After Post Exposure) 

2060 MPa

Elongation at break 
(ASTM D638)

3.4%

Heat deflection temp
(ASTM D648)

60°C

Storage 

10<t>50°C

Density

1.19 g/cm3