Daylight Pro Hard

Available Colours

Black

Strong, accurate parts with low shrinkage are made using our Pro Hard resin. This 3D printing resin produces stiff parts that cannot be easily deformed with compression or tension. Great for large scale applications where large models or even short run parts are required. The parts will display mechanical behaviour comparable to Polycarbonate/ABS blends.

Price 

£255

$357

Available in 5kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

440 cPs

Hardness 
(ASTM D2240 After post exposure)

86 Shore D

Tensile strength 
ASTM D638 (After post exposure, 1h UV)

46-53 MPa

Tensile modulus
ASTM D638 (After post exposure, 1h UV)

2200-2500 MPa

Elongation at break 
(After post exposure, 1h UV)

4-6%

Storage 

10<t>50°C

Density

1.18 g/cm3

Tough-Resin-Icon

Daylight Pro Tough New!

Available Colours

Amber

Extremely durable and resilient parts can be made using our 3D Pro Tough Resin. Printed parts will be strong and rigid, but capable of bending and flexing before displaying cracks or breaks. The 3D printed objects can bent using force, but will return to their original shape. 

Price 

£300

$420

Available in 5kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

600 cPs

Hardness 
(ASTM D2240 After post exposure)

80 Shore D

Tensile strength 
ASTM D638 (After post exposure)

35 MPa

Tensile strength 
ASTM D638 (Before post exposure)

10 MPa

Elongation at break 
(After post exposure, 1h UV)

50%

Storage 

10<t>50°C

Density

1.10 g/cm3

High-Tensile-Resin-Icon

Daylight Pro High Tensile

Available Colours

White

When strong parts are required, our unique Pro High Tensile is the resin of choice. Capable of producing incredibly detailed parts along with great strength, higher than that of injection moulded Polycarbonate with similar mechanical behaviour. Our 3D High Tensile Resin enables you to 3D print extremely strong and durable parts while maintaining an incredibly high accuracy.

Price 

£300

$420

Available in 5kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

440 cPs

Hardness 
(After post exposure)

86 Shore D

Tensile strength 
(ASTM D638 After Post Exposure, 1h UV)

46-53 MPa

Tensile Modulus
(ASTM D638 Before Post Exposure, 1h UV)

2200-2500 MPa

Elongation at break 

ASTM D638 (Postcured 120 mins UV and heat 60°C water)

4.8%

Storage 

10<t>50°C

Prosthetic-Leg 3D Printing

Firm-Resin-Icon

Daylight Pro Firm


Available Colours

Cream

If you need large parts that hold their shape whilst also being able to bend and flex slightly without snapping use our Pro Firm resin. These 3D printed parts will display similar properties to Polypropylene and the items will show great detail and malleability.

Price 

£255

$357

Available in 5kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

460 cPs

Hardness 
(ASTM D2240 After post exposure)

60 Shore D

Tensile strength 
(ASTM D638 After Post Exposure)

20 MPa

Tensile strength 
(ASTM D638 Before Post Exposure)

9 MPa

Elongation at break 
(ASTM D638 After Post Exposure)

20%

Storage 

10<t>50°C

Density

1.17 g/cm3

Photocentric Flexible Resin Icon

Daylight Pro Flexible

Available Colours

Amber

Large parts showing great flexibility can be printed using Pro Flexible resin. The 3D printed objects can be stretched without snapping or breaking, making this resin ideal for flexible applications. Thin or hollow structures can be bent or compressed and return to their original shape with ease. Ideal for creating parts where normal desktop printers can’t get to the right size that you need.

Price 

£255

$357

Available in 5kg bottles with non-drip cap. 

*Local Tax may apply

 

Viscosity
(At 25ºC Brookfield spindle 3)

200 cPs

Hardness 
(ASTM D2240 After post exposure)

85 Shore A

Tensile strength 
(ASTM D638 After Post Exposure)

4.9 MPa

Tensile strength 
(ASTM D638 Before Post Exposure)

1.5 MPa

Elongation at break 
(ASTM D638 After Post Exposure)

60%

Storage 

10<t>50°C

Density

1.18 g/cm3

Cleaner